MI 00 601 ................... download or print pdf 

DESCRIPTION:
Based on the MI 00 604 formulation, modifications have been made to the resin in order to increase the friction coefficient.


SOME TYPICAL APPLICATIONS:
Friction washers
Brakes pads
Static brakes.


ADHESIVES:
The use of any well known thermosetting adhesive is recommended.


RUBBING SURFACES:
Good quality, fine grained pearlitic cast iron with Brinell hardness of 150-200 is recommended.


PHYSICAL PROPERTIES:
Density g/cm3 .... 1.85–1.87
Hardness (SHORE-D) .... 80–85
Acetone extraction .... <2.5%
Ignition loss .... 42–44.5%


MECHANICAL PROPERTIES:
Tensile strength N/mm² .... 11.97
(ASTM D-638)

Compressive strength N/mm² .... 58.5
10% (UNE 53205)

Ultimate compressive strength .... 109.5
N/mm² (UNE 53205)



FRICTION PROPERTIES:
Friction coefficient (dynamic)µ
(See graph) .... 0.45 ± 0.05


Wear rate (@ 79N, 7m/s) F.A.S.T .... 45 - 85mm3 /Kwh



F.A.S.T. test conditions (max temperature)


F=79N v=7m/s t=90min ....<250ºC
F=100N v=7m/s t=
F=100N v=11m/s t=50min ....<320ºC


Recommended operating temperatures (max) :
Continuous operation .... 250 ºC
Intermittent operation .... 350 ºC


µ (friction coefficient) vs temperature @79N/7 m/s