.:Techniques Information:.
MI 00 605 ................... download or print pdf
DESCRIPTION:
Technology and experience, MI 00 605 has been developed from MI 00 602. This material has very good mechanical and frictional properties, and higher friction coefficient, shear and tensile forces than its parent material.
ADHESIVES:
The use of any well known thermosetting adhesive is recommended.
RUBBING SURFACES:
Good quality, fine grained pearlitic cast iron with Brinell hardness of 150-200 is recommended.
PHYSICAL PROPERTIES:
Density g/cm3 .... 1.80 ± 0.05
Hardness (SHORE-D) .... 84-90
Acetone extraction .... <2%
Ignition loss .... 38 – 44%
MECHANICAL PROPERTIES:
Tensile strength N/mm² .... 14.76
(ASTM D-638)
Compressive strength N/mm² .... 41.4
10% (UNE 53205)
Ultimate compressive strength .... 175
N/mm² (UNE 53205)
FRICTION PROPERTIES:
Friction coefficient (dynamic)µ
(See graph) .... 0.5 ± 0.05
Wear rate (@ 79N, 7m/s)
F.A.S.T .... 70 - 110mm3 /Kwh
F.A.S.T. test conditions (max temperature)
F=79N v=7m/s t=90min ....<250ºC
F=100N v=7m/s t=
F=100N v=11m/s t=50min ....<320ºC
Recommended operating temperatures (max) :
Continuous operation .... 250 ºC
Intermittent operation .... 350 ºC
µ (friction coefficient) vs temperature @79N/7 m/s
........................................................................ Torna su