DESCRIPTION:
Developed upon the base product MI 00 606
(incorporated of metal oxides in the compound), Sauleda “Short Fibre” technology has been used to produce a high friction material suited to constant operation.
SOME TYPICAL APPLICATIONS:
It is therefore suited to the less sensitive, high friction torque limiting and tension brake applications.
ADHESIVES:
The use of any well known thermosetting adhesive is recommended.
RUBBING SURFACES:
Good quality, fine grained pearlitic cast iron with Brinell hardness of 150-200 is recommended.
PHYSICAL PROPERTIES:
Density g/cm3 .... 1.80 ± 0.05
Hardness (SHORE-D) .... 81–89
Acetone extraction .... <2%
Ignition loss .... 40–48%
MECHANICAL PROPERTIES:
Tensile strength N/mm² .... 8.84
(ASTM D-638)
Compressive strength N/mm² .... 27
10% (UNE 53205)
Ultimate compressive strength .... 102.65
N/mm² (UNE 53205)
FRICTION PROPERTIES:
Friction coefficient (dynamic)µ
(See graph) .... 0.50 ± 0.05
Wear rate (@ 79N, 7m/s)
F.A.S.T .... 230±20 mm3 /Kwh
F.A.S.T. test conditions (max temperature)
F=79N v=7m/s t=90min ....<250ºC
F=100N v=7m/s t=
F=100N v=11m/s t=55min ....<336ºC
Recommended operating temperatures (max) :
Continuous operation .... 250 ºC
Intermittent operation .... 350 ºC
µ (friction coefficient) vs temperature @79N/7 m/s